Enhancement of reaction-sintering of alumina-excess magnesium aluminate spinel in presence of titania
【文件类型】 【消费金额】2.4 【文章页数】8 【会员操作】  
【文章作者】Sinhamahapatra, Somnath;Dana, Kausik;Tripathi, Himansu Sekhar
【文章摘要】      Alumina-excess magnesium aluminate spinel finds use in different high temperature applications including steel ladles. Alumina-excess spinel was prepared by solid oxide reaction using magnesia (MgO = 10 wt%) and calcined alumina (Al2O3 = 90 wt%), in the sintering temperature range of 1500-1700 degrees C. The role of titania on the densification, spinelisation, evolution of microstructure and phase assemblage was investigated in this MgOAl2O3 system. Titania addition increased the rate of densification 20x compared to undoped composition at 1500 degrees C under dynamic heating condition. However, under static firing, the beneficial effect of titania on densification could only be discerned at lower temperatures. The microstructure of titania doped sintered alumina excess spinel compacts contain magnesium aluminium titanate phase in the grain boundary of corundum and spinel grains. The beneficial effect of titania on densification is attributed to magnesium aluminium titanate phase (MgxAl2(1-x)Ti(1+x)O5) development and also by incorporation of Ti4+ into the spinel structure.
【关 键 字】
【卷】44【ISSUE】9【ISSUEID】815C0073    【文章期份】2018    【发布日期】2018/8/28 16:26:48    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有