Limitations of the hydrotalcite formation in Portland composite cement pastes containing dolomite and metakaolin
【文件类型】 【消费金额】5.1 【文章页数】17 【会员操作】  
【文章作者】Machner, Alisa;Zajac, Maciej;Ben Haha, Mohsen;Kjellsen, Knut O.;Geiker, Mette R.;De Weerdt, Klaartje
【文章摘要】      This study focuses on the reaction of dolomite powder in combination with metakaolin in Portland composite cement pastes. We studied paste samples cured at 20 degrees C, 38 degrees C, and 60 degrees C for up to 1 year. In these systems, the only magnesium-containing hydration phase of dolomite observed was hydrotalcite. Dolomite reacted notably already after 90 days when cured at 60 degrees C, whereas at lower curing temperatures the reaction was limited. The increased availability of aluminium due to the addition of metakaolin did not contribute to the formation of hydrotalcite. The refined pore space due to the metakaolin addition did not inhibit the hydrotalcite formation. However, the almost total absence of portlandite due to the pozzolanic reaction of the metakaolin inhibited the dolomite reaction, even in pastes with high porosity. Portlandite seems to be the driving force for the reaction as its absence is inhibiting the reaction to take place.
【关 键 字】
【卷】105【ISSUE】【ISSUEID】815C0068    【文章期份】2018    【发布日期】2018/8/28 16:25:37    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有