LaFeO3 ceramics as selective oxygen sensors at mild temperature
【文件类型】 【消费金额】2.1 【文章页数】7 【会员操作】  
【文章作者】Jaouali, Imen;Hamrouni, Hayfa;Moussa, Noomen;Nsib, Mohamed Faouzi;Angel Centeno, Miguel;Bonavita, Anna;Neri, Giovanni;Leonardi, Salvatore Gianluca
【文章摘要】      In this study, an investigation about the oxygen sensing properties of lanthanum orthoferrite (LaFeO3) ceramics is reported. LaFeO3 nanoparticles were synthesized by using tartaric sol-gel route and annealed in air at different temperatures (500, 700 and 900 degrees C). The samples have been characterized by using thermal analysis (TA), BET surface area and porosity, Fourier-transform infrared spectroscopy (FTIR), Raman spectroscopy, X-ray diffraction (XRD), and scanning electron microscopy (SEM). Results of sensing tests indicate that LaFeO3 nanoparticles exhibit good response to oxygen at mild temperatures (300-450 degrees C). The effect of annealing temperature on gas sensing performance was investigated, demonstrating that LaFeO3 ceramics obtained after annealing at 500 degrees C display better characteristics with respect to others. The oxygen sensor developed shows also high stability in humid environment and excellent selectivity to oxygen over other interfering gases such as CO, NO2, CO2, H-2 and ethanol.
【关 键 字】
【卷】44【ISSUE】4【ISSUEID】815C0073    【文章期份】2018    【发布日期】2018/8/28 16:25:21    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有