A model of splats deposition state and wear resistance of WC-10Co4Cr coating
【文件类型】 【消费金额】2.1 【文章页数】7 【会员操作】  
【文章作者】Han, Tao;Deng, Chunming;Zhang, Xiaofeng;Liu, Qiao
【文章摘要】      In this research both low temperature high velocity oxygen-fuel flame (LT-HVOF) and high velocity oxygen-fuel flame (HVOF) techniques were employed to prepare WC-10Co4Cr splats and coatings. In situ cutting of WC10Co-4Cr splats was carried out with focused ion beam (FIB), and a model was proposed to describe how the wear resistance of WC-10Co4Cr coatings was correlated with its residual stress state and the splats deposition state. It was observed that in LT-HVOF spraying process, WC-10Co4Cr splats were slightly melted showing "hill" shape, while in HVOF spraying process, the splats were half melted having the appearance of "concavity". The residual stress of WC-10Co4Cr coatings is determined by the size, melting state, flight speed and temperature gradient of splats. In this paper, the quantitative function formula involving heating temperature and the flight speed of the powder is put forward for the first time to predict the wear resistance of the WC-10Co4Cr coatings. This will provide a theoretical basis for engineering practice and an effective way to save costs.
【关 键 字】
【卷】44【ISSUE】4【ISSUEID】815C0073    【文章期份】2018    【发布日期】2018/8/28 16:25:19    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有