Study of crystal structure, dielectric, magnetic and magnetoelecrtic properties of xCoFe(2)O(4)-(1-x)Na0.5Bi0.5TiO3 composites
【文件类型】 【消费金额】2.4 【文章页数】8 【会员操作】  
【文章作者】Bhasin, Tanvi;Agarwal, Ashish;Sanghi, Sujata;Kotnala, R. K.;Shah, Jyoti;Yadav, Manisha;Tuteja, Muskaan
【文章摘要】      Multiferroic composites of spinel ferrite and ferroelectric xCoFe(2)O(4) - (1-x)Na0.5Bi0.5TiO3 (with x = 0.10,0.30,0.50) were efficiently prepared by standard solid state reaction mechanism. X-ray diffractometer was used to analyze crystal structure of the prepared composites. The observed XRD patterns of the composites comprise peaks of both the phases i.e. ferrite and ferroelectric, with no sign of secondary peaks. Rietveld refinement of XRD data further confirms the coexistence of these two phases with cubic (Fd3m) and rhombohedral (R3c) symmetry corresponding to ferrite and ferroelectric phase respectively. The 3-dimensional overview of crystal structure of pure CoFe2O4 and Na0.5Bi0.5TiO3 and of composite 0.50CoFe(2)O(4) - 0.50Na(0.5)Bi(0.5)TiO(3) is generated by using refined parameters. The dielectric constant (epsilon') and dielectric loss (tan delta) values were recorded as a function of frequency ranging from 100 Hz to 7 MHz and at different temperatures. Both epsilon' and tan delta follow dispersion pattern at lower frequencies while show frequency independent behavior at higher frequencies. The magnetic evaluation carried by analyzing M-H hysteresis loop reveals the ferrimagnetic characteristics of these composites. The highest value of magnetic moment is 1.12 mu(B) observed for composite 0.50CoFe(2)O(4) - 0.50Na(0.5)Bi(0.5)TiO(3). Magnetoelectric (ME) voltage coefficient (alpha) was also demonstrated to observe the interaction between ferrite and ferroelectric phases. The highest value of alpha (72.72 mu V/Oe cm) is obtained for low ferrite composition 0.10CoFe(2)O(4) - 0.90Na(0.5)Bi(0.5)TiO(3), which suggests the dependence of magnetoelectric response on the resistivity of the composites.
【关 键 字】
【卷】44【ISSUE】7【ISSUEID】815C0073    【文章期份】2018    【发布日期】2018/8/28 16:25:15    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有