A novel method for preparing dense diffusion barrier limiting current oxygen sensor
【文件类型】 【消费金额】2.1 【文章页数】7 【会员操作】  
【文章作者】Liu Tao;Jin Hongbin;Li Lin;Yu Jingkun
【文章摘要】      Abstract

A novel method for preparation of a dense diffusion barrier limiting current oxygen sensor is presented. The dense thin‐layer with the nominal composition Sr‐, Mg‐ and Fe‐doped lanthanum gallate (LSGMF) was prepared over La0.8Sr0.2Ga0.8Mg0.2O3–δ(LSGM) electrolyte by a thermal diffusion method. The crystal structure, morphology, elemental distribution, conductivity, and sensing performance of the prepared sample were investigated. X‐ray diffraction (XRD) analysis shows a highly crystalline perovskite.SEMEDSanalysis shows that the dense thin‐layer with about 40 μm thickness is well attached to the solid electrolyte. Electrical conductivity measurement shows that the dense thin‐layer has high conductivity of 8.73 S·cm?1at 800°C. The oxygen sensor exhibits good sensing performance. The variations of the limiting current (IL) vs oxygen content (x(O2)) can be obtained as follows:IL(mA)

【关 键 字】
【卷】101【ISSUE】4【ISSUEID】815B0005    【文章期份】2018    【发布日期】2018/8/28 16:25:11    点击率:0    打印    关闭
首页 新闻资讯 会议会展 视频培训 图书 期刊 外文期刊 报纸 标准 专利 成果 产品 企业 知识进厂
网络市场部:010-65761182 网络技术部:010-51164639  传真:010-65761182 Email:service@chinabmi.com
在线服务 QQ:  
建筑材料工业技术情报研究所 国家建材技术图书馆
京ICP备06002939号 京ICP备000046
Copyright © 2004 chinabmi.com All rights reserved. 中国建材智网版权所有